冻融与酸雨侵蚀共同作用下混凝土损伤分析

肖前慧1, 牛荻涛2   

  1. 1. 西安科技大学 建筑与土木工程学院, 陕西 西安 710054;
    2. 西安建筑科技大学 土木工程学院, 陕西 西安 710055
  • 收稿日期:2014-05-08 修回日期:2014-10-21 出版日期:2014-12-25 发布日期:2015-01-20
  • 作者简介:肖前慧(1981-),女,四川达州人,讲师,2010年在西安建筑科技大学获博士学位,现主要从事混凝土结构耐久性研究.E-mail:xiaohui_99@126.com
  • 基金资助:
    国家自然科学基金重点项目(50378079); 陕西省教育厅专项项目(2013JK0968)资助

Damage analysis of concrete subjected to both freezing-thawing cycles and acid rain attack

XIAO Qianhui1, NIU Ditao2   

  1. 1. Institute of Architecture and Civil Engineering, Xi'an University of Science and Technology, Xi'an 710054, China;
    2. Institute of Civil Engineering, Xi'an University of Architecture and Technology, Xi'an 710055, China
  • Received:2014-05-08 Revised:2014-10-21 Online:2014-12-25 Published:2015-01-20

摘要: 进行了快速冻融和酸雨侵蚀作用下的混凝土室内模拟试验, 研究了冻融和酸雨侵蚀作用下混凝土的质量损失和相对动弹性模量变化规律. 试验结果表明, 混凝土在冻融-酸雨复合环境下的损伤大于冻融作用下的损伤. 通过分析研究, 建立了冻融循环和酸雨侵蚀共同作用下不同水胶比混凝土的质量损失与冻融循环次数的函数关系及冻融与酸雨腐蚀共同作用下混凝土损伤演化方程, 为冻融环境混凝土结构耐久性设计与评估奠定了基础.

关键词: 混凝土, 酸雨侵蚀, 冻融循环, 损伤模型

Abstract: Based on the result of laboratory experiment for the concrete under the action of both rapid freezing-thawing cycles and acid rain and the study of quality loss process and relative elastic modulus behaves, the following conclusion can be drawn: the damage of concrete subjected to both freezing-thawing cycles and acid rain is greater than that subjected to freezing-thawing cycles alone. Through analysis and study, functional relationships between the quality loss and freezing-thawing cycles of the concrete with different water binder ratios under the action of both rapid freezing-thawing cycles and acid rain are established; concrete damage evolution equation under combined action of freezing-thawing cycles and acid rain is established too. All these results settle a foundation for durability assessment and design of concrete under freezing-thawing environment.

Key words: concrete, acid rain attack, freezing-thawing cycles, damage model